High Flame Retardant Cable Material Series for Building Wire Arrangement-High Flame Retardant Cable Material Series for Building Wire Arrangement-Products-Products-Hebei Zhonglian Polymer Technology Development Co., Ltd.
  • High Flame Retardant Cable Material Series for Building Wire Arrangement
    1.Product Names and Types
    Number
    Product
    Type
    Application
    1
    90℃Thermoplastic halogen-free low-smoke high flame-retardant POE sheath compound
    ZL1112-HG
    Can be used for building wires with high flame retardant requirement and emergency lighting wires, e.g. stores and five-star hotels. The products can no crackles the flame tests with national and IEC standards.
    2
    90℃hermoplastic halogen-free low-smoke high flame-retardant POE sheath compound
    ZL1112-HG-2
    3
    90℃Thermoplastic Low-smoke Halogen-free high Flame-retardant Polyolefin Insulating Compound
    ZL1112-JG-2
    4
    125℃Irradiation cross-linked halogen-free low-smoke high flame-retardant POE insulating compound
    ZL1214-JG-2
    5
    125℃Irradiation cross-linked halogen-free low-smoke high flame-retardant POE sheath compound
    ZL1214-HG-2

    2.Product Description
    2.1. Properties:
    The series of products are made of the main material polyolefin resin and auxiliaries such as halogen-free flame retardant and antioxygen, with the process of mixing, plasticizing and pelleting. The environmentally controlled substance of the materials such as heavy metal and halogen meet the requirement of RoHS environmental protection directive, according to the detection of SGS Company.
    The series of products are of good mechanical, physical, electrical and flame retardant properties as well as cabling process, which are in line with IEC603322, GB/T18380 and can meet the flame retardant test requirement of relevant standards of building wire and cable arrangement in other countries.

    2.2Machining Process
    2.2.1.The compound should dry before use.
    2.2.2.The compound recommended the halogen-free screw with a compression ratio of 1.25~2.0:1
    2.2.3.Extruding Temp
    Zone 1:110℃,Zone 2:130℃,Zone 3:140℃,Zone 4:150℃,Zone 5:150℃,Head:155-165℃

    Product Property Standards
    Item
    Unit
    Typical Value
    ZL1112-HG
    ZL1112-HG-2
    ZL1112-JG
    ZL1214-JG
    ZL1214-HG
    Density
    g/cm3
    1.50
    1.45
    1.49
    1.46
    1.46
    Shore Hardness
    A
    92
    95
    95
    95
    95
    Tensile strength
    Mpa
    12.85
    13.25
    13.45
    13.52
    13.65
    Elongation at Break
    %
    230
    190
    170
    190
    180
    Volume Resistivity at 20℃
    Ω·cm
    3.82×1013
    2.82×1014
    2.75×1014
    1.78×1014
    6.78×1013
    Air Thermal Aging Test
     
     
     
     
     
    Test Temp and Durative Tim
    ℃*h
    121*168
    121*168
    121*168
    158*168
    158*168
    Variation on Tensile Strength
    %
    +15
    +15
    +16.5
    +18.3
    +17.6
    Variation on Elongation at Break
    %
    -17.5
    -14.6
    -17.5
    -19.6
    -18.5
    Oxygen Index
    %
    35
    35
    36
    36
    36
    Dielectric Strength
    MV/m
    25
    25
    25
    25
    25
    Low temp Impact Test
    -45
    -45
    -30
    -40
    -35
    PH
     
    5.3
    5.3
    5.3
    5.2
    5.3
    Conductivity
    μs/mm
    1.5
    1.5
    1.5
    1.5
    1.7
    Smoke Density
     
     
     
     
     
     
    No Smoke Dmw
     
    125
    190
    170
    135
    130
    Smoke Dmy
     
    56
    56
    56
    60
    60